Gas Diffusion Layer
Toray TCP-H is a Carbon-Carbon Composite Paper which has been used for PAFC and PEFC for decades and has proven durability. Its high mechanical strength, conductivity and gas permeability are suitable for use as a Gas Diffusion Layer (GDL) in fuel cell applications.
Characteristics
• High strength
• Excellent gas permeability and low electrical resistivity
• Good handling
• Minimal electrochemical corrosion
Electrode base material for fuel cell physical properties table
Product No. | Thickness (mm) | Electrical resistance m-cm | Thermal conductivity W/(m . K) | Gas permeability ml . mm/(cm² . hr . mmAq) | Porosity (%) | Bulk density (g/cm3) | Surface roughness (um) | Linear expansion coefficient (Planar direction) (25 – 100°C) (x10-6/°C) | Flexural strenght (MPa) | Flexural modulus (GPa) | Tensile Strenght (kgf/cm) | |||
Thickness direction | Planar direction | Thickness direction (room temperature) | Planar direction (room temperature) | Planar direction (100°C) | ||||||||||
TGP-H-030 | 0,11 | 80 | – | – | – | – | 2500 | 80 | 0,4 | 8 | -0,8 | 40 | 8 | – |
TGP-H-060 | 0,19 | 80 | 5,8 | -1,7 | 21 | 23 | 1900 | 78 | 0,44 | 8 | -0,8 | 40 | 10 | 5 |
TGP-H-090 | 0,28 | 80 | 5,6 | -1,7 | 21 | 23 | 1700 | 78 | 0,44 | 8 | -0,8 | 40 | 10 | 7 |
TGP-H-120 | 0,37 | 80 | 4,7 | -1,7 | 21 | 23 | 1500 | 78 | 0,45 | 8 | -0,8 | 40 | 10 | 8 |